1000c Fire Retardant Polyurethane PU Coated High Silica Fiberglass Fabric

Product Description

Product Description

High Silica Fiberglass Fabric is made by silica fiberglass fabric which is a kind of inorganic fiber contaiting more than 96% SiO2. It is high temperature resistance. Its softening point approaches 1700°C and can be used at 1000°C for a long time. It can work short-term at 1500°C. Silica fabric is applicable for use as a high temperature resistant, heat resistant, fire resistant,and corrosion resistant material.It is widely used in avaiation and aerospace, metallurgy, chemical, building material and fire fighting industry. Apart from applications requiring high temperature-resistance, it is also has insulation and fire prevention uses. Such as Thermal insulation covers, padding, lagging, welding blanket, fire curtain and other heavy duty fire control system. Silica cloth is suitable for coating with difference elastomers and polymers.

Product Parameters

 

Model No.	Thickness (mm)	Width (mm)	Weight (g/m2)	Weave	Roll length (meters)	Color
HS-026-P	0.26	820	240g	Plain	100	White
HS-065-P	0.65	860	590		50
HS-076-P	0.76	860	680		50
HS-100-P	1	860	915		50
HS-135-P	1.35	860	1250		50
HS-065-T	0.65	920	590	Satin	46	White / Golden
HS-065-T	0.65	1500	590		46
HS-076-T	0.76	920	680		46
HS-100-T	1	920	915		46
HS-135-T	1.35	920	1250		46

Product Features

Advantages
1. Fire Resistant, heat resistance
2..Extremely high-temperature resistance up to 1500 C
3.Good anti-abrasion, easy to be cut, sewn and fabricated
4. Durability, High Strength, Corrosion Resistant

Application

Main application
--Heat and flange shielding,insulation jackets,cover,mattress,pad
--Fire Doors,fire curtain,welding blankets,fire blankets
--Hose and cable protection
--- Protective garments
--Stress relief
--Gasket, seal
-- Car
 

Related Products

Silicone rubber coated silica fbaric is silica fabric coated one side or both sides with silicone rubber. The material has a higher strength base fabric and higher temperature capability compared to conventional welding fabric, making it suitable for heavy-duty protection of personnel and equipment. Moreover, the coated material exhibits outstanding abrasion resistance.

Silicone Coated Silica Fabrics for industrial application requiring a compromise of thermal protection and abrasion resistance properties.


Properties:

• Strong and durable
• Water and Oil Repellent 
• good sealing performance
• High Dimensional Stability
• Good Chemical & Media Resistance
• Outstanding electrical properties
• Superior water, oil and heat resistance. 
• Easy to cut, fabricate and work with

Applications:

• Welding/fire blankets and curtains
• Fire Doors and Curtains.
• Pump, Flange and Valve Covers
• High Temperature Pipe Lagging
• Steam Pipe Insulation
• Outer layer for Insulation jackets, mattress, and pad
• Bellows and Ductwork Connectors
• Fabric expansion joints
• High-temperature gaskets and seals
• For Protective Barriers and Heat Shields

Item No.	Coating	Norminal Weight		Norminal Thickness	Weave Pattern	Standard Width(cm)	Base Fabric Tensile strength(N/INCH)		Fabric Yarn	Working Temperature(ºC)
		gsm	osy	mm			warp	weft		fabric	coating
SLS420	2 sides	420	12.4	0.35	Twill 3*1	92	>300	>250	96% silica	1000	260-280
SLS500	2 sides	500	14.7	0.4	Twill 3*1	92	>300	>250	96% silica	1000	260-280
SLS760	2 sides	760	22.4	0.75	Satin 8HS	92/100/127	>600	>500	96% silica	1000	260-280
SLS810	2 sides	810	23.9	0.75	Satin 8HS	92/100/127	>600	>500	96% silica	1000	260-280
SLS870	2 sides	870	25.7	0.8	Satin 8HS	92/100/127	>600	>500	96% silica	1000	260-280

Polyurethane (PU) coated Silica Fabric is made of fiberglass which is woven by high quality high silica filament yarns, and then coated with Polyurethane (PU) on single side or both sides, finally colored with aluminum pigments.

Item No.	Coating	Norminal Weight		Norminal Thickness	Weave Pattern	Standard Width(cm)	Base Fabric Tensile strength(N/INCH)		Fabric Yarn	Working Temperature(ºC)
		gsm	osy	mm			warp	weft		fabric	coating
SLP420	2 sides	430	12.7	0.41	Satin 4HS	92	>300	>250	96% silica	1000	260-280
SLP630	2 sides	630	18.6	0.63	Satin 8HS	92/100	>500	>350	96% silica	1000	260-280

Properties:

• Strong and durable
• Water and Oil Repellent 
• good sealing performance
• High Dimensional Stability
• Good Chemical & Media Resistance
• Outstanding electrical properties
• Superior water, oil and heat resistance. 
• Easy to cut, fabricate and work with

PU coated fiberglass fabric features good rebound resilience, toughness, softness,good abrasion & allergen resistance, oils resistance, cold,aging and weather resistance,and anti-solvents, and water proof.it can withstand temperature up to 180ºC for short bursts,this kind of cloth has lots of positive properties,bright in color,  It also has the function of an anti bacterium,and can also be used for mould proofing, heat-insulation and anti-ultraviolet.

Polyurethane 1 side Coating style Glass Fiber Fabric

Inspection item	Technical index
Weight	460g/m^2	620g/m^2	690g/m^2	690g/m^2	1070g/m^2
Thickness	0.4mm	0.77mm	0.63mm	0.7mm	1.2mm
Temperature resistance	-50ºC~180ºC
Color	Green,Silver
Fabric style	Fiberglass with steel reinforced,Fiberglass
Fire resistance	Non-flammable(NF92507,M0)
Applications	Insulation jackets,mattress and Pad,fabric expansion joints,fabric ductwork connector,fire doors&fire curtains,welding/fire blankets.

Polyurethane both side Coating style Glass Fiber Fabric

Inspection item	Technical index
Weight	220g/m^2	460g/m^2	640g/m^2	720g/m^2	720g/m^2	880g/m^2
Thickness	0.21mm	0.4mm	0.86mm	0.7mm	0.72mm	0.9mm
Temperature resistance	-50ºC~180ºC
Color	Red/white color,yellow/green color,grey/white color,blue/black color,silver grey color,white,red,black,yellow,blue,green,silver grey
Fabric style	Fiberglass with steel reinforced,fiberglass
Fire resistance	Non-flammable(NF92507,M0)
Applications	Insulation jackets,mattress and Pad,fabric expansion joints,fabric ductwork connector,fire doors&fire curtains,welding/fire blankets

Storage

Unless otherwise specified, the fiberglass products should be in dry, cool and moisture-proof area. The room temperature and humidity should be always maintained at 15ºC~35ºC and 35%~65%. It is best if the price is used within 12 months after production date. The fiberglass products should remain in their original packaging until just prior to user.

Application

          24 Hours Services          

Choose us, you will get the key of market!
Contact us, we will use the professional knowledge serve you!
Wish we can create the great future together!